wear resistant coatings > BD765 anti heat anti abrasion corrosion resistant coatings

BD765 anti heat anti abrasion corrosion resistant coatings

BD765 high temperature anti abrasion corrosion resistant epoxy ceramic coatings

Product description:
BD765 high temperature anti abrasion corrosion resistant coating is the high performance interpenetrating network
structure high temperature resistant,wear resistant polymeric ceramic material which compounded by high performance
wear resistant,corrosion resistant materials(like ceramic,silicon carbide,carborundum,titanium alloy etc) and inorganic
high temperature adhesives.Widely used in the preparation of wear resistant coatings on the surfaceof various machine
parts which have high temperature,abrasion resistant requirements.The highest temperature resistant is 600 degree.

Product features:
1.With excellent wear resistant and corrosion resistant performance
2.With high bonding strength to the metal substrates
3.Convenient for construction,without very high technology requirements for the constructors.
4.Suitable for the protection of high temperature corrosion and abrasion working condition.
5.It can be blade coating directly for both the facade and ceiling,Don't drip and slide,don’t need support.
6.The cured products are water resistant,acid and alkali resistant.

Performance Index:

Product item		Physical states	Operation time limit(25℃)		Usable time	Range of application
BD765 high temperature anti wear corrosion resistant coating		paste	40 min		5-7 days	Used in the preparation of anti abrasion corrosion resistant coating on the surface of various machine part which has high temperature wear resistant requirements under the temperature of 600 degree, such as various dry wet gas flue and holder
Color	Density (g/cm3)	Compressive strength (Mpa) GB1041-2008		Tensile strength (Mpa) GB6329-2009	Shear strength (Mpa) GB7124-2008		Working temperature（℃）
greyish white	1.8	65			4.2		-60-600

How to use:
1.Surface treatment:Do the roughing treatment on the pending-repair part,grinding with angle grinder or sand blasting etc.The surface after roughing treatment should be cleaned,
the surface after this treatment should be the one roughen,dry and fresh substrates,should be no greasy dirt and dust.

2.Preparation: Mix them according to the weight ratio A:B=3:1,then stir it uniformly,and use it up within 40 minutes,
generally it’s while construction and configuring adhesives,every time the largest quantity of configuring adhesive is
not more than 20 kilograms,too much adhesive is solidified too fast,hasn’t been used up until the partial adhesive has
solidified and can’t be used.According to the actual temperature,the configuration can be proper some more in winter,
and proper some less in summer.

3.Coating: The suitable coating thickness of BD765 high temperature anti abrasion corrosion resistant coating is 2-4mm,
should make the mixed-up materials be coating on the pending-repair parts layer by layer,the first layer should be compacted,make it infiltrate fully with the substrates.
The thickness of each layer should be controlled under 2mm,should be coating the next layer after the upper layer drying,
the coating time of the front and behind layers is depend on the temperature during construction and the coating thickness.
When the coating thickness is 0.5mm,the coating time is more than 10 hours in winter,and the coating time is more than 4
hours in summer.We should insist the principle:coating on the next layer after the upper layer drying

4.Curing: After the coating is coated in the specified size,we should place it for 5-7 days,it can be put into using after
doing the curing

Packaging Details:
Packed in a plastic drum, two-component,10Kg/group,A component: 7.5Kg/drum, B component: 2.5Kg/kettle.

Storage and Warranty:
Store it in the cool and dry place,keep away from moisture.The warranty period is 12 months.